WELDING WIRE

WELDING WIRE

»»会社概要　»»事業方針　»»事業概要　»»基本スケジュール　»»基本料金体系

 

气体保护焊丝ER49-1  药性焊丝

  • 下記をSEIKA SHOPにて販売致しております。

GAS SHIELDING WELDING WIRE（在庫品）

ガスシールドアーク溶接用ソリッドワイヤ

  • 品番：Y H５０−６
  • 規格：GB／T8110-2008　ER50-6　AWS ER70S -6     JIS  Z3312　YGW12相当
  • 線径：0.8mm, 0.9mm, 1.0mm, 1.2mm(20kg／箱，250kg／ドラム)
  • 製造：中国製

系列商品の詳細

Packaging Wire Size Spool Size Net Weight
φ0.8~1.6(mm) D100mm D200mm D270mm D300mm K300mm 1kg、5kg、15kg、18kg、20kg
chemical composition of welding wire(%) C Mn Si P S Cr Ni Cu
0.06~0.15 1.40~1.85 0.80~1.15 ≤0.025 ≤0.035 – – ≤0.50
Mechanical Properties or Deposited Metal Yield strengthσ0.2(Mpa) Tensile strengthσb(Mpa) Elongationδ5(%) AKV impact(J)
≥420 ≥500 ≥22 ≥27(-29)
Wire Size(mm) φ0.8 φ1.0 φ1.2 φ1.6 Welding position
Welding current(A) 40~140 50~220 80~350 120~550
Please be noted Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust.
Before welding please clean out the oil,rust,water etc from the work parts

FLUX-CORED WELDING WIRES（受注生産）

E81T1-NI2

E500T-1, E70T-1
Uses: terms welding, low-alloy steel and 490Mpa grade high strength steel, typically used for shipbuilding, marine structures, steel structures, bridges, chemical welding equipment, etc.
Standard:
GB / T: E500T-1
AWS: E70T-1
Package Specification Silk panel Net weight
Φ1.0~1.6(mm) D100mm D200mm D270mm D300mm K300mm 1 kg, 5 kg, 15 kg, 18 kg, 20 kg
ChemicalWireIngredients(%) C Mn Si P S
≤0.10 ≤1.75 ≤0.75 ≤0.03 ≤0.03
Deposited metalMechanical properties
 Yield strengthσ0.2(Mpa) Tensile strengthσb(Mpa) Elongationδ5(%) AKV impact energy (J)
≥400 ≥480 ≥22 ≥47(0℃)
Wirediameter(mm) φ1.2 φ1.4 φ1.6 Welding position
Welding current(AMP.)  120~300 160~400 190~450
Notes: 1 wire into the plant must be stored in a dry environment,not just open the disk waterproof wire welding package 2should be removed before welding surface of the oil, rust,moisture and other impurities
3. The use of CO2 gas, CO2 gas purity of 99.98%.
4 CO2 protection welding gas flow should be controlled in20-25L/min.
5 out of wire length should be controlled at 15-25mmrange.
6 to be preheated before welding to 150-300 ℃, after welding to be tempered by 700-740 ℃. 
E501T-1, E71T-1
Use is CO2 flux cored wire for welding titanium. High deposition efficiency, excellent all-position welding performance can also be vertical down welding. For ships, pressure vessels, mechanical equipment, steel bridges,steel low carbon steel and 490MPa grade high strength steel welding. Standard:
GB / T: E501T-1
AWS: E71T-1
Package Specification Silk panel Net weight
Φ1.0~1.6(mm) D100mm D200mm D270mm D300mm K300mm 1 kg, 5 kg, 15 kg, 18 kg, 20 kg
ChemicalWireElement(%) C Mn Si P S  
≤0.10 ≤1.75 ≤0.75 ≤0.03 ≤0.03  
Deposited metalMechanical properties Yield strengthσ0.2(Mpa) Tensile strengthσb(Mpa) Elongationδ5(%) AKV Impact Energy(J)
≥400 ≥480 ≥22 ≥47(0℃)

≥47(-20℃)
Wirediameter(mm) Φ1.0 φ1.2 φ1.4 φ1.6 Welding position
Welding current(AMP.) 80~250 120~300 160~400 190~450
Notes: 1 wire into the plant must be stored in a dry environment,not just open the disk waterproof wire welding package 2should be removed before welding surface of the oil, rust,moisture and other impurities
3. The use of CO2 gas, CO2 gas purity of 99.98%.
4 CO2 protection welding gas flow should be controlled in20-25L/min.
5 out of wire length should be controlled at 15-25mmrange.
6 to be preheated before welding to 150-300 ℃, after welding to be tempered by 700-740 ℃. 

seikajp

コメントを投稿するには、以下のいずれかでログインしてください。

Gravatar
WordPress.com ロゴ

WordPress.com アカウントを使ってコメントしています。 ( ログアウト /  変更 )

Facebook の写真

Facebook アカウントを使ってコメントしています。 ( ログアウト /  変更 )

キャンセル

%s と連携中

%d人のブロガーが「いいね」をつけました。